WABO®Crete II - Joint Header (Elastomeric Concrete)

"THE ORIGINAL! New Zealand's most reliable and preferred elastomeric concrete header product!"

Wabo®Crete II is a two-component polyurethane expansion joint header with specialty aggregate, 100% solids material for use in exterior construction environments. Wabo®Crete II is a unique mixture which monolithically bonds the expansion joint to the deck, creating a waterproof system. Wabo®Crete II absorbs traffic impact loads and evenly disperses them into the deck, while allowing the system to flex with deck loads. It is resistant to ozone, UV, deicing chemicals, and abrasives. The addition of heat is not required to increase flow or cure the material. It will self-level in the block-out.
RECOMMENDED FOR:
  • As an expansion joint header/nosing for various expansion joint systems (Bridges / Carparks)
  • Spall repair of existing joint headers/nosing applications.
  • Void filler
FEATURES Include:
  • Fast turn-around - temperature depending, it can accept vehicular traffic after 1 hour
  • Two component polyurethane header material with a specialty aggregate
  • Resistant to ozone, de-icing chemicals and abrasives
  • Self-leveling, ambient cure material
  • Absorbs traffic impact loads
NOTES:
  1. Specimens are cast discs with a 2.5" diameter and 0.375" thickness. Specimens are conditioned for four hours at test temperatures. A one pound steel ball is dropped onto the center of the specimen through a plastic tube from an initial height of 5 feet. The drop height is increased by intervals until the specimen cracks.
  2. The briquette is sawed in half so that the cut surface area equals approximately 1 square inch. Surface is blasted and placed in a mold. WaboCrete II is cast against it. Specimen is submerged in water (seven days at room temperature). Using a riehle Briquette tester,  failure of the specimen is considered to occur at either the bond interface or within one of the two materials.